{"id":8124,"date":"2026-10-07T10:00:00","date_gmt":"2026-10-07T02:00:00","guid":{"rendered":"https:\/\/maxtormetal.com\/?p=8124"},"modified":"2026-10-07T22:31:22","modified_gmt":"2026-10-07T14:31:22","slug":"grid-blade-snapping-slot-fillet-radius-r02mm-fix","status":"publish","type":"post","link":"https:\/\/maxtormetal.com\/ja\/grid-blade-snapping-slot-fillet-radius-r02mm-fix\/","title":{"rendered":"\u30b9\u30ea\u30c3\u30c8\u6e9d\u5e95\u306b\u304a\u3051\u308b\u30b0\u30ea\u30c3\u30c9\u5203\u306e\u6298\u640d\u9632\u6b62\u7b56\uff1aR\u22650.2 mm \u8a2d\u8a08\u306b\u5411\u3051\u305f\u6e9d\u5e95R\u534a\u5f84\u3001EDM\u653e\u96fb\u52a0\u5de5\u9762\u306e\u5065\u5168\u6027\u3001\u304a\u3088\u30732\u56de\u713c\u304d\u623b\u3057\u71b1\u51e6\u7406\u7ba1\u7406"},"content":{"rendered":"
\"Schematic<\/figure><\/div>

\u30af\u30a4\u30c3\u30af\u30b5\u30de\u30ea\u30fc\uff1a<\/strong> \u30b9\u30ea\u30c3\u30c8\u6e9d\u5e95\u306b\u304a\u3051\u308b\u30b0\u30ea\u30c3\u30c9\u5203\uff08\u30b9\u30ea\u30c3\u30c8\u5203\uff09\u306e\u6298\u640d\u306f\u30013\u3064\u306e\u8981\u56e0\u306e\u76f8\u4e57\u52b9\u679c\u306b\u3088\u3063\u3066\u5f15\u304d\u8d77\u3053\u3055\u308c\u307e\u3059\u3002\u305d\u308c\u306f\u3001\u92ed\u89d2\u30b9\u30ea\u30c3\u30c8\u306b\u3088\u308b\u9ad8\u3044\u5f3e\u6027\u5fdc\u529b\u96c6\u4e2d\uff08Kt 7\u301c12\uff09\u3001\u30af\u30e9\u30c3\u30af\u306e\u767a\u751f\u6e90\u3068\u306a\u308b\u8868\u9762\u6b20\u9665\uff08EDM\u653e\u96fb\u5909\u8cea\u5c64\u3084\u7814\u524a\u3084\u3051\u3069\uff09\u3001\u304a\u3088\u3073\u57fa\u6750\u306e\u976d\u6027\uff08\u9ad8\u9771\u6027\uff09\u4e0d\u8db3\u3067\u3059\u3002\u4e3b\u8981\u306a\u5de5\u5b66\u7684\u5bfe\u7b56\u3068\u3057\u3066\u306f\u3001\u6e9d\u5e95R\u534a\u5f84\u3092R\u22650.2 mm\u306b\u898f\u5b9a\u3059\u308b\u3053\u3068\uff08\u3053\u308c\u306b\u3088\u308aR0.05 mm\u5f62\u72b6\u3068\u6bd4\u8f03\u3057\u3066\u5fdc\u529b\u96c6\u4e2d\u4fc2\u6570Kt\u304c\u7d04\u534a\u5206\u306b\u4f4e\u6e1b\u3057\u307e\u3059\uff09\u3001\u30bb\u30ab\u30f3\u30c9\u30ab\u30c3\u30c8\uff08\u30b9\u30ad\u30f3\u30ab\u30c3\u30c8\uff09\u3084\u7814\u78e8\u306b\u3088\u308bEDM\u5909\u8cea\u5c64\uff08\u767d\u5c42\uff09\u306e\u5b8c\u5168\u9664\u53bb\u3001\u304a\u3088\u3073\u92fc\u7a2e\u306b\u5fdc\u3058\u305f\u9069\u5207\u306a2\u56de\u713c\u304d\u623b\u3057\uff08\u30c0\u30d6\u30eb\u30fb\u30c6\u30f3\u30d1\u30fc\uff09\u71b1\u51e6\u7406\u7ba1\u7406\u3092\u7d44\u307f\u5408\u308f\u305b\u308b\u3053\u3068\u304c\u6319\u3052\u3089\u308c\u307e\u3059\u3002\u786c\u5ea6HRC 56\u301c58\u306e\u30c0\u30a4\u30b5\u30fc\u7528\u30b9\u30ea\u30c3\u30c8\u5203\u306e\u9069\u7528\u4e8b\u4f8b\u3067\u306f\u3001\u6e9d\u5e95R\u3092R0.20 mm\u306b\u7ba1\u7406\u3059\u308b\u3053\u3068\u3067\u3001\u7a81\u767a\u7684\u306a\u5203\u7269\u4ea4\u63db\u3092\u7d0455\u301c65%\u524a\u6e1b\u3057\u3001\u8a08\u753b\u5916\u306e\u8a2d\u5099\u505c\u6b62\u6642\u9593\u3092\u7d0445\u301c55%\u524a\u6e1b\u3059\u308b\u3053\u3068\u306b\u6210\u529f\u3057\u307e\u3057\u305f\u3002<\/p><\/blockquote>

\u30b0\u30ea\u30c3\u30c9\u30b9\u30ea\u30c3\u30c8\u5203\u306e\u6298\u640d\u306f\u3001\u9ad8\u901f\u30b9\u30ea\u30c3\u30c8\u5207\u65ad\u304a\u3088\u3073\u30b0\u30ea\u30c3\u30c9\u30ab\u30c3\u30c8\u5de5\u7a0b\u306b\u304a\u3044\u3066\u3001\u6700\u3082\u751f\u7523\u3092\u963b\u5bb3\u3057\u3001\u304b\u3064\u539f\u56e0\u304c\u8bef\u89e3\u3055\u308c\u3084\u3059\u3044\u30c8\u30e9\u30d6\u30eb\uff08\u5931\u6548\u5f62\u5f0f\uff09\u306e\u4e00\u3064\u3067\u3059\u3002\u5203\u7269\u304c\u30b9\u30ea\u30c3\u30c8\u306e\u6e9d\u5e95\u3067\u7834\u65ad\u3059\u308b\u3068\u3001\u8a08\u753b\u5916\u306e\u8a2d\u5099\u505c\u6b62\u3001\u521d\u56de\u5408\u683c\u7387\uff08FPY\uff09\u306e\u4f4e\u4e0b\u3001\u305d\u3057\u3066\u30b3\u30a4\u30eb\u6761\u6750\u306b\u5bfe\u3059\u308b\u4e8c\u6b21\u7684\u306a structural\/quality \u4e0d\u5177\u5408\u306e\u6ce2\u53ca\u3068\u3044\u3063\u305f\u81f4\u547d\u7684\u306a\u5f71\u97ff\u304c\u5373\u5ea7\u306b\u767a\u751f\u3057\u307e\u3059\u3002\u9023\u7d9a\u30b3\u30a4\u30eb\u52a0\u5de5\u30e9\u30a4\u30f3\u3092\u7d71\u62ec\u3059\u308b\u88fd\u9020\u30de\u30cd\u30fc\u30b8\u30e3\u30fc\u3084\u65b9\u3005\u306b\u3068\u3063\u3066\u3001\u305f\u3063\u305f1\u56de\u306e\u5203\u7269\u6298\u640d\u4e8b\u6545\u304c\u6570\u6642\u9593\u306b\u53ca\u3076\u4fee\u7e55\u51fa\u623b\u308a\u4f5c\u696d\u3092\u5f15\u304d\u8d77\u3053\u3057\u3001\u6708\u9593\u306e\u5229\u76ca\u7387\u3092\u5727\u8feb\u3059\u308b\u30b9\u30af\u30e9\u30c3\u30d7\uff08\u6b69\u7559\u307e\u308a\u60aa\u5316\uff09\u640d\u5bb3\u3092\u767a\u751f\u3055\u305b\u307e\u3059\u3002<\/p>

\u305d\u306e\u6839\u672c\u539f\u56e0\u306f\u3001\u8a2d\u8a08\u6bb5\u968e\u3067\u7d44\u307f\u8fbc\u307e\u308c\u305f\u5fdc\u529b\u96c6\u4e2d\u3001\u3042\u308b\u3044\u306f\u691c\u51fa\u3055\u308c\u306a\u304b\u3063\u305f\u5de5\u7a0b\u4e0a\u306e\u6b20\u9665\uff08\u52a0\u5de5\u6b20\u9665\uff09\u3067\u3042\u308b\u30b1\u30fc\u30b9\u304c\u307b\u3068\u3093\u3069\u3067\u3059\u3002\u30b9\u30ea\u30c3\u30c8\uff08\u6e9d\uff09\u4ed8\u304d\u5203\u7269\u306b\u304a\u3044\u3066\u3001\u6e9d\u5e95\u306f\u5203\u7269\u672c\u4f53\u306e\u4e2d\u3067\u6700\u3082\u9ad8\u3044\u5fdc\u529b\u304c\u52a0\u308f\u308b\u90e8\u4f4d\u3068\u306a\u308a\u307e\u3059\u3002\u9069\u5207\u306a\u5e7e\u4f55\u5b66\u5f62\u72b6\u306e\u7ba1\u7406\u3068\u91d1\u5c5e\u7d44\u7e54\u306e\u5341\u5206\u306a\u976d\u6027\u304c\u78ba\u4fdd\u3055\u308c\u3066\u3044\u306a\u3044\u5834\u5408\u3001\u9045\u304b\u308c\u65e9\u304b\u308c\u7834\u65ad\uff08\u30af\u30e9\u30c3\u30af\uff09\u304c\u767a\u751f\u3059\u308b\u3053\u3068\u306b\u306a\u308a\u307e\u3059\u3002<\/p>

\u89e3\u6c7a\u7b56\u306f\u4e8c\u6761\u306e\u5de5\u5b66\uff08\u30a8\u30f3\u30b8\u30cb\u30a2\u30ea\u30f3\u30b0\uff09\u6226\u7565\u306b\u3042\u308a\u307e\u3059\u3002\u7b2c\u4e00\u306b\u3001\u30b9\u30ea\u30c3\u30c8R\u90e8\uff08\u6e9d\u5e95\uff09\u306e\u5fdc\u529b\u96c6\u4e2d\u4fc2\u6570\uff08Kt\uff09\u3092\u78ba\u5b9f\u306b\u4f4e\u6e1b\u3055\u305b\u308b\u305f\u3081\u3001\u6e9d\u5e95R\u534a\u5f84\u3092R\u22650.2 mm\u306b\u898f\u5b9a\u3057\u691c\u8a3c\u3059\u308b\u3053\u3068\u3002\u7b2c\u4e8c\u306b\u3001\u305d\u306eR\u5f62\u72b6\u5468\u8fba\u306e\u57fa\u6750\u976d\u6027\u3092\u6700\u5927\u9650\u306b\u9ad8\u3081\u308b\u305f\u3081\u3001\u7cbe\u5bc6\u306b\u8abf\u6574\u3055\u308c\u305f2\u56de\u713c\u304d\u623b\u3057\uff08\u30c0\u30d6\u30eb\u30fb\u30c6\u30f3\u30d1\u30fc\uff09\u71b1\u51e6\u7406\u3092\u9069\u7528\u3059\u308b\u3053\u3068\u3067\u3059\u3002\u3053\u308c\u3089\u4e21\u6226\u7565\u3092\u652f\u3048\u308b\u306e\u304c\u3001\u5de5\u5177\u30fb\u5203\u7269\u306e we Procurement\uff08\u8abf\u9054\uff09\u6642\u306b\u898b\u843d\u3068\u3055\u308c\u304c\u3061\u306a3\u3064\u306e\u5de5\u7a0b\u7ba1\u7406\u3067\u3059\u3002\u305d\u308c\u306f\u3001EDM\u653e\u96fb\u5909\u8cea\u5c64\u306e\u5b8c\u5168\u9664\u53bb\u3001\u53b3\u683c\u306a\u7814\u524a\u3084\u3051\u3069\uff08\u7814\u524a\u71b1\u640d\u50b7\uff09\u306e\u9632\u6b62\u3001 processing \u6700\u7d42\u691c\u67fb\u524d\u306e\u6b8b\u7559\u5fdc\u529b\u9664\u53bb\uff08\u30b9\u30c8\u30ec\u30b9\u30ea\u30ea\u30fc\u30d5\uff09\u306e\u5fb9\u5e95\u3067\u3059\u3002<\/p>

\u6280\u8853\u30ce\u30fc\u30c8\uff1a<\/strong> If your specification for slotted grid blades requires documented fillet radius verification, EDM process records, and heat-treat batch traceability, see Maxtor Metal’s reference page on \u9762\u53d6\u308a\u52a0\u5de5\u3055\u308c\u305f\u5de5\u696d\u7528\u30d6\u30ec\u30fc\u30c9\u7528\u92fc\u5e2f\uff08\u30ea\u30fc\u30eb\u5165\u308a\uff09<\/em><\/strong><\/a> for supply specifications and documentation standards applicable to precision slotted blade geometries.<\/p>

\u672c\u8a18\u4e8b\u3067\u306f\u3001\u3053\u306e\u4e8c\u6761\u306e\u6226\u7565\u306e\u5404\u8981\u7d20\u3092\u9806\u6b21\u89e3\u8aac\u3057\u307e\u3059\u3002\u6e9d\u5e95\u306b\u304a\u3051\u308b\u7834\u65ad\u306e\u6a5f\u69cb\uff08\u30e1\u30ab\u30cb\u30ba\u30e0\uff09\u3001\u6e9d\u5e95R\u5f62\u72b6\u304c\u5fdc\u529b\u96c6\u4e2d\u4fc2\u6570\uff08Kt\uff09\u3092\u5b9a\u91cf\u7684\u306b\u4f4e\u6e1b\u3055\u305b\u308b\u4ed5\u7d44\u307f\u3001\u30ef\u30a4\u30e4\u653e\u96fb\u52a0\u5de5\uff08EDM\uff09\u304a\u3088\u3073\u7814\u524a\u52a0\u5de5\u306b\u304a\u3051\u308b\u54c1\u8cea\u7ba1\u7406\u57fa\u6e96\u3001\u92fc\u7a2e\u306b\u5fdc\u3058\u305f\u713c\u304d\u623b\u3057\uff08\u30c6\u30f3\u30d1\u30fc\uff09\u6761\u4ef6\u306e\u9078\u5b9a\u65b9\u6cd5\u3001\u305d\u3057\u3066\u5203\u7269\u304c\u5b9f\u7a3c\u50cd\u306b\u5165\u308b\u524d\u306e\u6700\u7d42\u691c\u8a3c\u30c1\u30a7\u30c3\u30af\u30dd\u30a4\u30f3\u30c8\u306b\u3064\u3044\u3066\u7db2\u7f85\u3057\u307e\u3059\u3002<\/p>

\u306a\u305c\u30b9\u30ea\u30c3\u30c8\u6e9d\u5e95\u306f\u30b0\u30ea\u30c3\u30c9\u5203\uff08\u7db2\u76ee\u72b6\u5207\u65ad\u5203\uff09\u304c\u6700\u3082\u6298\u640d\u3057\u3084\u3059\u3044\u90e8\u4f4d\u306a\u306e\u304b<\/h2>
\"\u306a\u305c\u30b9\u30ea\u30c3\u30c8\u6e9d\u5e95\u306f\u30b0\u30ea\u30c3\u30c9\u5203\uff08\u7db2\u76ee\u72b6\u5207\u65ad\u5203\uff09\u304c\u6700\u3082\u6298\u640d\u3057\u3084\u3059\u3044\u90e8\u4f4d\u306a\u306e\u304b\"<\/figure><\/div>

Stress Concentration at Slot Bottoms<\/h3>

In a slotted blade under bending or cyclic cutting loads, stress is not distributed uniformly across the cross-section. It concentrates sharply at geometric discontinuities \u2014 and no feature on a slotted blade creates a sharper discontinuity than a tight slot root.<\/p>

The theoretical stress concentration factor Kt relates the peak local stress \u03c3 max to the nominal applied stress \u03c3 nom:<\/p>

Kt = \u03c3 max \/ \u03c3 nom<\/strong><\/p><\/blockquote>

For a rectangular slot in a finite plate, Kt is strongly influenced by the ratio of the root radius r<\/em> to the slot half-width b<\/em> (or depth t<\/em>, depending on the reference model). When r<\/em> approaches zero \u2014 as it does with a square-cornered slot \u2014 Kt climbs toward singularity. Even at r<\/em> = 0.05 mm, Kt values of 8\u201312 are common in tight-slot geometries at industrial blade scales. At those multipliers, a nominal bending stress of 300 MPa becomes a local stress exceeding 2,400 MPa \u2014 well above the fracture toughness threshold for most high-carbon tool steels in the hardened-and-lightly-tempered condition.<\/p>

The slot bottom is therefore not just a stress concentration \u2014 it is the single most failure-critical feature in the tool design. Every process decision downstream of design \u2014 EDM strategy, grinding pass depth, tempering protocol, final inspection \u2014 must be evaluated in the context of what it does to that slot root.<\/p>

Crack Initiation Sources in Slots<\/h3>

Even with adequate fillet geometry, cracks can initiate at slot bottoms when surface or subsurface defects provide nucleation sites. The three most consequential defect sources in slotted blade manufacture are:<\/p>

1. EDM recast (white) layer.<\/strong> Wire-EDM and sinker-EDM are standard processes for producing slots in hardened or semi-hardened tool steel. Both leave a resolidified, amorphous surface layer typically 2\u201325 \u00b5m thick. This layer is harder and more brittle than the base matrix \u2014 Vickers hardness values above 1,100 HV are common \u2014 and it contains tensile residual stresses and microcracks from the rapid resolidification thermal cycle. These microcracks are structural initiators under cyclic load. If left in place, they can propagate into the substrate within the first few thousand blade strokes.<\/p>

2. Grinding-induced microcracks.<\/strong> Aggressive grinding after EDM \u2014 particularly with insufficient coolant delivery or excessive wheel speed \u2014 generates localized heat that causes surface temper, re-hardening, or micro-cracking. In the slot root geometry, where wheel access is restricted, coolant starvation is a persistent process risk.<\/p>

3. Quench-induced residual tensile stress.<\/strong> During hardening, differential thermal contraction between the blade surface and core \u2014 particularly in the thin-wall regions around slots \u2014 generates residual tensile stresses. Without adequate stress-relief tempering, these stresses add directly to applied service stresses, reducing the effective fracture margin.<\/p>

Role of Residual Tensile Stress<\/h3>

Residual stress is invisible to the inspector who uses only a hardness tester and a visual check. But it is fully additive to applied stress in the fracture-mechanics sense. A slot bottom carrying 150 MPa of residual tensile stress from quench shrinkage, combined with a 300 MPa applied bending stress and a Kt of 6, experiences a local stress state of approximately:<\/p>

\u03c3 local \u2248 Kt \u00d7 (\u03c3 applied + \u03c3 residual) = 6 \u00d7 450 MPa = 2,700 MPa<\/p><\/blockquote>

Most high-alloy tool steels in service condition have plane-strain fracture toughness (KIC) between 20 and 35 MPa\u00b7m\u2070\u00b7\u2075 \u2014 but the range is wide because it spans different grades and heat-treat states.<\/p>

For reference: D2 (1.2379) at HRC 58\u201362 typically shows KIC of 18\u201322 MPa\u00b7m\u2070\u00b7\u2075; M2 (1.3343) at HRC 62\u201365 is typically 20\u201325 MPa\u00b7m\u2070\u00b7\u2075; H13 (1.2344) at HRC 44\u201350 (lower hardness, higher toughness application) can reach 28\u201338 MPa\u00b7m\u2070\u00b7\u2075. When selecting a blade grade for a slotted geometry application, the KIC value at the intended service hardness \u2014 not an average range \u2014 is the relevant design input.<\/p>

\u6e9d\u5e95R\uff08\u30d5\u30a3\u30ec\u30c3\u30c8\u534a\u5f84\uff09\u306e\u69cb\u9020\u8a2d\u8a08<\/h2>
\"\u6e9d\u5e95R\uff08\u30d5\u30a3\u30ec\u30c3\u30c8\u534a\u5f84\uff09\u306e\u69cb\u9020\u8a2d\u8a08\"<\/figure><\/div>

Why R\u22650.2 mm Reduces Kt<\/h3>

The relationship between fillet radius and Kt is nonlinear: the benefit is largest in the lower radius range, meaning the transition from R0.05 mm to R0.2 mm delivers a larger Kt reduction than the transition from R0.5 mm to R1.0 mm.<\/p>

Using normalized stress concentration charts from Pilkey & Pilkey, Peterson’s Stress Concentration Factors<\/em> (3rd ed., Wiley, 2008) for a slot in a finite-width plate under in-plane loading:<\/p>

Slot Root Radius r (mm)<\/th>Approximate Kt (typical slot geometry)<\/th><\/tr>
0.05<\/td>10\u201312<\/td><\/tr>
0.10<\/td>7\u20138<\/td><\/tr>
0.20<\/td>4.5\u20135.5<\/td><\/tr>
0.30<\/td>3.5\u20134.0<\/td><\/tr>
0.50<\/td>2.5\u20133.0<\/td><\/tr><\/tbody><\/table><\/figure>

The move from R0.05 mm to R0.20 mm cuts Kt roughly in half. If the material’s fracture resistance is held constant, halving Kt more than doubles the load-carrying capacity before crack initiation. Alternatively, at equivalent loads, halving Kt can extend fatigue life by an order of magnitude or more, depending on the fatigue crack growth exponent for the specific steel grade.<\/p>

R0.2 mm is therefore a practical engineering minimum<\/strong>, not an arbitrary specification. It is the radius below which Kt rises sharply enough that even modest process variation \u2014 residual stress, surface defects, minor EDM recast remnants \u2014 pushes the slot bottom into reliable fracture territory.<\/p>

Selecting Radius and Tolerances<\/h3>

Selecting the target radius requires balancing three competing constraints:<\/p>

  1. Stress concentration reduction<\/strong> \u2014 a larger r<\/em> is always mechanically beneficial.<\/li>\n\n
  2. Slot dimensional function<\/strong> \u2014 the slot must still guide the strip or lock the grid pattern correctly. A root that is too large can interfere with a mating feature or alter the spring rate of thin blade webs.<\/li>\n\n
  3. Manufacturability<\/strong> \u2014 the radius must be achievable and measurable by the processes in use (EDM skim cut, grinding, polishing).<\/li><\/ol>

    For most industrial grid blade geometries, a target of R0.20 \u00b1 0.05 mm<\/strong> is achievable with wire-EDM skim cuts followed by stone polishing, and is tight enough to maintain slot function while achieving the required Kt reduction. In thicker blades with deeper slots, R0.30\u20130.50 mm may be practical and should be evaluated where slot function permits.<\/p>

    Specify the tolerance unilaterally on engineering drawings: the minimum radius is the structural requirement; the maximum is a fit\/function constraint. A notation of R0.20 min \/ R0.30 max makes this explicit and avoids the common shop-floor ambiguity of “rounding out the corner” without a defined upper limit.<\/p>

    Measuring and Verifying Radii<\/h3>

    Slot root radii in the R0.2\u2013R0.5 mm range require instrument-grade measurement. Acceptable methods include:<\/p>